| 1 | EFFECTS OF MICROSTRVCTURE ON FATIGUE CRACK GROWTH BEHMIOR IN Ni-BASE SUPERALLOY GH586显示文摘Threshold stress values, muging from ~8 to 16MPa·m1/2 can be obtained in a Ni-base alloy GH586 by varying the microstructure through heat treatments. The threshold and low crack growth rate behaviors at room temperature, with varying groin size and γ’-distribution, have been investigated. The results indicate that grain size is an important microstructurol parameter that affects fatigue crack growth threshold and propagation behaviors, as the values of △Kth increase with increasing grain size, but the γ’ -distribution also has important effect. Analyses show that the effects of groin size on threshold and low crack-growth rate behavior result from heterogeneous deformation and roughness-induced crack closure due to crystallographic slipping and cracking in coarse microstructure. The higher △Kth and lower fatigue crack growth rate with increasing amounts of fine γ’ phases are closely related to less damage accumulation level in deformation zone of crack-tip resulted from heterogeneous deformation due to dislocations’ shearing γ’ precipitates. | S.S. Xie X.F. Pan T.L. Wang Z.X. Wang H.C. Yang and Q. Wang ( School of Materials and Metallurgy, Northeastern Universityl Shenyang 110006, China)( School of Materials and Metallurgy, Northeastern Universityl Shenyang 110006, China)( School of Materia | 1999 | Acta Metallurgica Sinica(English Letters)1999，12，3： | 5 |
您所在的机构暂未开通此部分的功能，请联系管理员