| 1 | Removal of formaldehyde over Mn_xCe_(1- x)O_2 catalysts: Thermal catalytic oxidation versus ozone catalytic oxidation显示文摘MnxCe1-xO2(x:0.3–0.9)prepared by Pechini method was used as a catalyst for the thermal catalytic oxidation of formaldehyde(HCHO).At x=0.3 and 0.5,most of the manganese was incorporated in the fluorite structure of Ce O2to form a solid solution.The catalytic activity was best at x=0.5,at which the temperature of 100%removal rate is the lowest(270°C).The temperature for 100%removal of HCHO oxidation is reduced by approximately 40°C by loading 5 wt.%Cu Oxinto Mn0.5Ce0.5O2.With ozone catalytic oxidation,HCHO(61 ppm)in gas stream was completely oxidized by adding 506 ppm O3over Mn0.5Ce0.5O2catalyst with a GHSV(gas hourly space velocity)of 10,000 hr-1at 25°C.The effect of the molar ratio of O3to HCHO was also investigated.As O3/HCHO ratio was increased from 3 to 8,the removal efficiency of HCHO was increased from 83.3%to 100%.With O3/HCHO ratio of 8,the mineralization efficiency of HCHO to CO2was 86.1%.At 25°C,the p-type oxide semiconductor(Mn0.5Ce0.5O2)exhibited an excellent ozone decomposition efficiency of 99.2%,which significantly exceeded that of n-type oxide semiconductors such as Ti O2,which had a low ozone decomposition efficiency(9.81%).At a GHSV of 10,000 hr-1,[O3]/[HCHO]=3 and temperature of 25°C,a high HCHO removal efficiency(≥81.2%)was maintained throughout the durability test of 80 hr,indicating the long-term stability of the catalyst for HCHO removal. | Jia Wei Li Kuan Lun Pan Sheng Jen Yu Shaw Yi Yan Moo Been Chang | 2014 | Journal of Environmental Sciences2014，26，12： | 9 |
您所在的机构暂未开通此部分的功能，请联系管理员