| 2 | SYNTHESIS OF CoFe_(2)O_(4)/Pb(Zr_(0.53)Ti_(0.47))O_(3)MULTIFERROIC COMPOSITE THICK FILMS BY LOW-SINTERING-TEMPERATURE SCREEN PRINTING METHOD显示文摘CoFe_(2)O_(4)/Pb(Zr_(0.53)Ti_(0.47))TO_(3)(abbreviated as CFO/PZT)multiferroic composite thick films were successfully fabricated on alumina substrate with gold bottom electrode by screen printing method at a low-sintering temperature.The processing included the modi fication and dispersion of ferromagnetic CFO powder and ferroelectric PZT powder,the preparation of uniform pastes,and the selection of proper annealing temperature for composite thick films.Transmission electron microscopic pictures(TEM)indicated the submicron meter of particles size for both CFO and PZT particles.After annealing at 900℃ for 1 h in air,tape test con firmed the quality of multiferroic thick films as well as pure CFO and PZT films.X-ray diffraction(XRD)showed a coexistence of CFO and PZT phases;furthermore,a smooth surface was observed through scanning electron microscopic(SEM)pictures along with the sharp cross-sectional picture,indicative of 100m of film thickness.Ferromagnetic and ferroelectric properties were observed in CFO/PZT films simultaneously at room temperature.Compared with the reported CFO/PZT multiferrroic thin films,the present ferromagnetic property was closing to that of the chemical solgel synthesized film and even that from the physical pulsed laser deposition technique.However,the ferroelectric property showed a degenerated behavior,possible reasons for this was discussed and further optimization was also proposed for the potential multifunctional application. | W.CHEN C.X.HUANG T.S.YAN W.ZHU Z.P.LI X.F.CHEN O.K.TAN | 2011 | Journal of Advanced Dielectrics2011，1，1： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员