| 1 | Microstructural evolution and superelastic properties of ultrafine-graine d NiTi-base d shape memory alloy via sintering of amorphous ribbon precursor显示文摘NiTi-based shape memory alloys(SMAs)are considered as cutting-edge intelligent functional materials.However,it remains a great challenge to obtain ultrafine-grained(UFGed)bulk materials with mm-scale size as well as outstanding superelastic properties.Here,UFGed bulk Ti_(35)Zr_(15)Ni_(35)Cu_(15)NiTi-based SMA is successfully prepared via spark plasma sintering of amorphous ribbon precursor at different sintering temperatures,and microstructural evolution and superelastic properties are symmetrically investigated.It is found that its grain size ranges from UFG to micro-grain with increased sintering temperature regard-less of the predominant B2 matrix in all bulk samples.Interestingly,the orientation relationships between B2 matrix and nano-scale fcc(Ti,Zr)_(2)Ni precipitate evolve from coherent to incoherent.Consequently,the UFGed samples exhibit perfect superelasticity with the high recoverable strain of∼5.8%,the stable recov-ery rate above 99%,and the great critical stress inducing martensitic transformation higher than 1 GPa,far superior to the corresponding ones of suction-cast micro-grained TiZrNiCu SMAs.Fundamentally,the perfect superelasticity is attributed to the good resistance to dislocation slip or grain boundary slip by residual nano-scale amorphous phase or secondary phase of coherent and semi-coherent fcc(Ti,Zr)_(2)Ni precipitate.In addition,the gentle superelastic plateau is associated to the favorable transfer stress and the strong ability to accommodate dislocation movement,which is generated by the coherent interface between nano-scale fcc(Ti,Zr)_(2)Ni and UFGed B2 matrix.These results suggest that spark plasma sintering of amorphous alloy precursor is a feasible route to obtaining excellent superelasticity in NiTi-based SMAs. | W.S.Cai H.Z.Lu H.Z.Li Z.Liu H.B.Ke W.H.Wang C.Yang | 2023 | Journal of Materials Science & Technology2023，，7： | 2 |
您所在的机构暂未开通此部分的功能，请联系管理员