| 1 | A novel method to prepare amorphous alloy catalyst with silver including and KBH4 reducing显示文摘 | Keyi Tao Wei Li | 2004 | Catalysis Communication2004，，： | 1 |
| 2 | Advances in chemical synthesis and application of metal-metalloid amorphous alloy nanoparticulate catalysts显示文摘This paper reviews the advances in the chemical synthesis and application of metal-metalloid amorphous alloy nanoparticles consisting of transition metal(M)and metalloid elements(B,P).After a brief introduction on the history of amorphous alloy catalysts,the paper focuses on the properties and characterization of amorphous alloy catalysts,and recent developments in the solution-phase synthesis of amorphous alloy nanoparticles.This paper further outlines the applica-tions of amorphous alloys,with special emphasis on the problems and strategies for the application of amorphous alloy nanoparticles in catalytic reactions. | WU Zhijie LI Wei ZHANG Minghui TAO Keyi | 2007 | Frontiers of Chemical Science and Engineering2007，1，1： | 1 |
| 3 | Characterization and catalytic application of homogeneous nano-composite oxides ZrO2-Al2O3 显示文摘 | Li Guoran Li Wei Tao Keyi | 2004 | Catalysis Today2004，，93： | 1 |
| 4 | Morphology and hydrodesulfurization activity of CoMo sulfide supported on amorphous ZrO2 nanoparticles combined with Al2O3 显示文摘 | Li Guoran Li Wei Tao Keyi | 2004 | Applied Catalysis A : General2004，273，： | 1 |
| 5 | Catalytic dechlorination of monochlorobenzene with a new type of nanoscale Ni(B)/Fe(B) bimetallic catalytic reductant显示文摘 | Yi Han Wei Li Minghui Zhang Keyi Tao | 2008 | Chemosphere2008，，1： | 1 |
| 6 | Catalytic Dehydration of 4-Hydroxy-3-hexanone to 4-Hexen-3-one over HZSM-5 Zeolite显示文摘A study on catalytic dehydration of 4-hydroxy-3-hexanone(HH)to 4-hexen-3-one(HO)was carried out through conversion of HH over HZSM-5 zeolite catalyst in a fixed-bed reactor(FBR)operating under atmospheric pressure.The test indicated a relatively high activity of the HZSM-5 zeolite capable of achieving a HH conversion of 99.2%and a HO yield of 83.5%.Catalyst deactivation could be prevented by increasing the reaction temperature by 10℃for every 20 h and adding 2.0%of piperidine in the feed.A catalyst stability test(for 100 h)in FBR showed that the catalyst was active even after 100 h of time-on-stream with HH conversion remaining at 99.2%and HO yield still reaching over 83.5%.Regeneration experiment showed that the regenerated catalyst demonstrated a catalytic performance comparable to the fresh one. | Huang Kai Zheng Haitao Tao Keyi | 2013 | China Petroleum Processing & Petrochemical Technology2013，15，4： | 0 |
| 7 | Hydrogenation of furfuryl alcohol to tetrahydrofurfuryl alcohol on NiB/SiO_(2) amorphous alloy catalyst显示文摘NiB/SiO2 amorphous alloy catalyst was prepared by power electroless plating method and characterized by induction coupled plasma(ICP),Brunauer–Emmett–Teller method(BET),transmission electron microscope(TEM)and X-ray diffraction(XRD)techniques.The catalytic perfor-mance of NiB/SiO2 was investigated for the hydrogenation of furfuryl alcohol(FA)to tetrahydrofurfuryl alcohol(THFA).The effects of operational conditions,such as reaction tem-perature,pressure,and stirring rate were carefully studied.The proper conditions were determined as the following:pressure 2.0 MPa,temperature 120°C and stirring rate 550 r/min.A typical result with FA conversion of 99%and THFA selectivity of 100%was obtained under such conditions,which was close to that over Raney Ni. | SONG Yun LI Wei ZHANG Minghui TAO Keyi | 2007 | Frontiers of Chemical Science and Engineering2007，1，2： | 0 |