| 1 | A hidden precipitation scenario of theθ’-phase in Al-Cu alloys显示文摘Al-Cu binary alloys are important and interesting industry materials.Up to date,the formation mechanisms of the key strengthening precipitates,namedθ’-phase,in the alloys are still controversial.Here,we report that for non-deformed bulk Al-Cu alloys theθ’-phase actually has its own direct precursors that can form only at elevated aging temperature(>ca.200℃).These high-temperature precursors have the same plate-like morphology as theθ’-phase precipitates but rather different structures.Atomicresolution imaging reveals that they have a tetragonal structure with a=0.405 nm and c=1.213 nm,and an average composition of Al_(5-x)Cu_(1+x)(0≤x<1),being fully coherent with the Al-lattice.This precursor phase may initiate with a composition of Al5 Cu and evolve locally towards Al_(4)Cu_(2)in composition,eventually leading to a consequent structural transformation into theθ’-phase(Al4 Cu2=Al2 Cu).There are evidences that because of their genetic links in structure,such a high-temperature precursor may transform to theθ’-phase without having to change their morphology and interface structure.Our study reveals a well-defined and previously hidden precipitation scenario for theθ’-phase to form in Al-Cu alloys at an elevated aging temperature. | L.Zhou C.L.Wu P.Xie F.J.Niu W.Q.Ming K.Du J.H.Chen | 2021 | Journal of Materials Science & Technology2021，，16： | 4 |
您所在的机构暂未开通此部分的功能，请联系管理员