题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | De-twinning and Texture Change in an Extruded AM30 Magnesium Alloy during Compression along Normal Direction显示文摘Twinning and de-twinning are the salient deformation mechanisms in hexagonal close-packed(hcp)metals. The aim of this study was to examine and quantify the de-twinning process involving a reversible motion of twin boundaries in an extruded AM30 magnesium alloy after re-compression along the normal direction(ND) of pre-compressed samples along the extrusion direction(ED). {1012} extension twins were first introduced at a compressive strain of 3.7% along the ED. The subsequent compressive deformation along the ND induced a gradual shrinkage of twins with increasing cumulative true strain,and the complete de-twinning occurred at a strain of ~7.7%. The twin width decreased linearly with increasing true strain. Texture measurements verified the rotation of c-axes of hcp unit cells towards the anti-compression direction due to {1012} extension twinning after compression along the ED, and a gradual return of c-axes to the initial orientation due to twin shrinking or de-twinning during the following compression along the ND. The {1012} twinning corresponded to the formation of new texture components C{1210}<0001> and D{0110}<0001> and a decrease in the initial texture components A{0001}<2110> and B{0001}<1010>, while the twin shrinking or de-twinning was characterized by a gradual vanishing of components C{1210}<0001> and D{0110}<0001> and an increase in the components A{0001}<2110> and B{0001}<1010>. | D.Sarker J.Friedman D.L.Chen | 2015 | Journal of Materials Science & Technology2015，31，3： | 8 |
| 2 | 动态塑性变形下AZ31镁合金的孪生特征显示文摘沿热轧退火态AZ31镁合金轧制方向进行室温动态塑性变形,采用场发射扫描电子显微镜研究{10ī2}孪生的变体类型及结构特征。结果表明:在{10ī2}孪生机制主导塑性变形的初级阶段(ε<8%),AZ31镁合金中大部分晶粒内部仅产生一种{10ī2}孪生变体或变体对,所以孪晶结构呈彼此平行状,将晶粒分割成片层组织;这种片层组织的厚度随着应变量的增加而减小,从5.55μm减小到2.49μm;少数晶粒形核产生不同的{10ī2}孪生变体,且这种晶粒的数量随着塑性变形量的增大而增加;当ε>8%,孪生体积分数接近饱和,位错滑移成为镁合金主要的变形机制。 | 娄超 张喜燕 任毅 | 2015 | 中国有色金属学报2015，25，10： | 5 |
| 3 | 高应变速率下等径角挤压高纯粗晶铝中的形变孪晶与退火孪晶显示文摘在室温下对铸态高纯粗晶铝进行一道次高应变率动态等径角挤压(D-ECAP)变形,利用电子背散射衍射技术(EBSD)研究挤压过程中所形成的孪晶。结果表明:利用D-ECAP能够在粗晶铝中同时制备出形变孪晶和退火孪晶,但两者在形态、Kernel平均取向差(KAM)以及与相邻晶粒的取向差三个方面存在较大差异。D-ECAP高应变率和大剪切变形使高层错能铝中形成了百微米级的形变孪晶,形变孪晶的形态为透镜状,后续变形使得孪晶界偏离∑3 60°〈111〉取向关系且KAM值主要集中于0.6°~1.8°。高应变率剪切变形下形成的大量层错和复杂的位错组态以及高形变储存能在变形温升的作用下促进了退火孪晶的形成。退火孪晶的形态较不规则,但孪晶界的取向关系更接近于∑3 60°〈111〉且KAM值主要集中于0.2°~0.5°。 | 刘敬勇 卢磊 钟政烨 | 2021 | 材料工程2021，49，4： | 3 |
| 4 | 镁合金AZ91D化学机械抛光工艺研究显示文摘将化学机械抛光技术(Chemical Mechanical Polishing,CMP)引入到镁合金片的抛光中,以硅溶胶、表面活性剂、螯合剂及p H调节剂为原料,以涡流搅拌的方法制备镁合金(AZ91D)抛光液。采用单因素法分析抛光过程中压力、转速、抛光液流量及抛光时间等参数对抛光效果的影响。实验结果表明:在压力为0.06MPa,抛光盘上盘转速为10r/min、下盘转速为50r/min,抛光液流量为160m L/min,抛光时间为8min的条件下,镁合金表面形貌良好;在此工艺条件下经过化学机械抛光后,镁合金表面粗糙度Ra能达到10nm。 | 黄华栋 卞达 杨大林 赵永武 吴冬燕 | 2017 | 现代制造工程2017，，2： | 3 |
| 5 | 缓蚀剂在镁合金化学机械抛光过程中的作用显示文摘利用碱性体系抛光液研究了十二烷基苯磺酸钠(SDBS)缓蚀剂对镁合金化学机械抛光过程和抛光效果的影响。采用能谱仪XPS分析缓蚀剂在镁合金表面形成的膜层成分,并通过腐蚀试验、电化学分析和磨粒粒径测试的手段分析了抛光液中SDBS在镁合金化学机械抛光过程中的作用机理。结果表明:当SDBS含量为1.0%时,抛光液中SDBS可有效抑制镁合金在抛光过程中的腐蚀,缓释效果可达91%。SDBS与镁合金通过缩合反应生成保护膜,减小抛光后的表面粗糙度以及点蚀的出现,提高表面质量;另外,SDBS对Al2O3抛光磨粒具有一定的吸附作用。当SDBS含量为1.0%时,能有效抑制Al2O3磨粒团聚,进而对抛光效果产生一定的影响,减少抛光过程中划痕的产生。 | 杨大林 卞达 赵治安 倪自丰 赵永武 | 2015 | 陕西师范大学学报(自然科学版)2015，43，2： | 1 |