| 1 | Microstructure evolution and mechanical properties of linear friction welded S31042 heat-resistant steel显示文摘S31042 heat-resistant steel was joined by linear friction welding(LFW) in this study. The microstructure and the mechanical properties of the LFWed joint were investigated by optical microscopy, scanning electronic microscopy, transmission electron microscopy, hardness test and tensile test. A defect-free joint was achieved by using LFW under reasonable welding parameters. The dynamic recrystallization of austenitic grains and the dispersed precipitation of NbCrN particles resulting from the high stress and high temperature in welding, would lead to a improvement of mechanical property of the welded joint.With increasing the distance from the weld zone to the parent metal, the austenitic grain size gradually increases from ~1μm to ~150μm, and the microhardness decreases from 301 HV to 225 HV. The tensile strength(about 731 MPa) of the welded joint is comparable to that of the S31042 in the solution-treated state. | Yanmo Li Yongchang Liu Chenxi Liu Chong Li Zongqing Ma Yuan Huang Zumin Wang Wenya Li | 2018 | Journal of Materials Science & Technology2018，34，4： | 5 |
| 2 | In situ investigation on densification mechanism of Ti-20Al-19Nb(at.%)alloy by TiH2-assisted pressureless sintering显示文摘Dense Ti-20Al-19Nb(at.%)alloys can be cost-effectively fabricated by TiH_(2)-assisted pressureless sintering;nevertheless,the densification mechanism remains controversial without understanding the entire sintering process.By in situ observing the surface morphology of the Ti/Al/Nb and Ti/TiH_(2)/Al/Nb compacts upon heating,the densification mechanism of the Ti-20Al-19Nb alloys was elucidated in this study.In addition to the reported reason that the dehydrogenation of TiH_(2)provided reactive Ti,the densification of Ti-20Al-19Nb alloy was found to be strongly associated with the phase transformations upon sintering.The TiH_(2)participated in the reverse eutectoid transformation,α-Ti+δ-TiH_(2)→β-Ti,inducing theα/βand TiH_(2)/βgrain boundaries for the rapid diffusion of Al.The reaction of Ti(s)+Al(s)→TiAl_(3)(s)was then accelerated,and the majority of the Al phase was consumed in the solid state,which significantly reduced the pores from the transient liquid Al.The activation energy of the Ti-Al reaction decreased with the addition of TiH_(2),and the growth mode of the TiAl_(3)phase was changed.By removing the large pores at 700℃,the Ti-Al intermetallic phases were well connected,forming the continuous interdiffusion route for Ti,Al,and Nb.The diffusion of Nb,as well as the phase transformation ofα2→B2,was then promoted,and the ripening time for the B2 phase was increased.As a result,the density and mechanical properties were improved.The initial results of this study provided a foundation for the cost-effective fabrication of high-strength Ti-Al alloys containing refractory elements. | Qi Cai Qilin Yu Xinyao Li Yao Lu Yanmo Li Ganggang Cui | 2023 | Journal of Materials Science & Technology2023，，34： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员