| 1 | Ductility enhancement of EW75 alloy by multi-directional forging显示文摘In this study,the Mg-7Gd-5Y-1Nd-0.5Zr alloy can reach a high ductility by the process of multi-directional forging,and the evolution of the microstructure,texture and the mechanical properties were discussed systematically.The results show that after the solutionized sample was multi-forged at 500℃,its grain size can be refined from 292 um to 58 um.As the forging temperature decreased,fine particles precipitated in the matrix.The volume fraction of the particles increased with the forging temperature decreasing,so the nucleation and growth of crystallization were strongly restricted.There was no recrystallization as the forging temperature fell to 410℃,and the severe deformed grains distributed as streamlines perpendicular to the final compression axis.The texture intensity decreased with increasing forging passes.The sample with best ductility was obtained after compressed at 470℃,with an elongation to failure of 21%at room temperature,which is increased by 200%,in comparison with that of the samples in solutionized condition.EBSD results revealed that the mean grain size was 15 um.Refined grains as well as the weakened texture were the key factors to its high ductility. | M.Hong D.Wu R.S.Chen X.H.Du | 2014 | Journal of Magnesium and Alloys2014，2，4： | 4 |
| 2 | Coating behavior and surface hardening of Pd_(77)Cu_6Si_(17) thin film metallic glass on AZ31 magnesium alloy显示文摘Pd77Cu6Si17(PCS) thin film metallic glasses(TFMGs) with high glass forming ability and hardness were selected as a hard coating for improving the surface hardness of AZ31 magnesium alloy. Both microindentation and nanoindentation tests were conducted on specimens with various PCS film thicknesses from 30 to 2000 nm. The apparent hardness and the relative indentation depth(β) were integrated using a quantitative model. The interaction parameters involved and relative hardness values were extracted from iterative calculations. According to the results, surface hardness can be enhanced greatly by PCS TFMGs in the shallow region, followed by gradual decrease with increasing β ratio. In addition, specimens with thinner coatings(e.g., 200nm) showed greater substrate-film interaction and those with thick coatings(e.g., 2000nm) became prone to film cracking. The optimum TFMG coating thickness in this study was estimated to be around 200 nm. | X.H.DU Y.C.CHANG H.J.PEI B.Y.CHEN M.C.KUO J.C.HUANG | 2013 | Journal of Zhejiang University-Science A(Applied Physics & Engineering)2013，14，12： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员