3篇
您的检索式：作者名="Si Bingjun"
|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Rapid repair techniques for severely earthquake-damaged circular bridge piers with flexural failure mode显示文摘In this study, three rapid repair techniques are proposed to retrofit circular bridge piers that are severely damaged by the flexural failure mode in major earthquakes. The quasi-static tests on three 1:2.5 scaled circular pier specimens are conducted to evaluate the efficiency of the proposed repair techniques. For the purpose of rapid repair, the repair procedure for all the specimens is conducted within four days, and the behavior of the repaired specimens is evaluated and compared with the original ones. A finite element model is developed to predict the cyclic behavior of the repaired specimens and the numerical results are compared with the test data. It is found that all the repaired specimens exhibit similar or larger lateral strength and deformation capacity than the original ones. The initial lateral stiffness of all the repaired specimens is lower than that of the original ones, while they show a higher lateral stiffness at the later stage of the test. No noticeable difference is observed for the energy dissipation capacity between the original and repaired pier specimens. It is suggested that the repair technique using the early-strength concrete jacket confined by carbon fiber reinforced polymer(CFRP) sheets can be an optimal method for the rapid repair of severely earthquake-damaged circular bridge piers with flexural failure mode. | Sun Zhiguo Li Hongnan Bi Kaiming Si Bingjun Wang Dongsheng | 2017 | Earthquake Engineering and Engineering Vibration2017，16，2： | 8 |
| 2 | Rapid repair of severely earthquake-damaged bridge piers with flexural-shear failure mode显示文摘An experimental study was conducted to investigate the feasibility of a proposed rapid repair technique for severely earthquake-damaged bridge piers with flexural-shear failure mode. Six circular pier specimens were first tested to severe damage in flexural-shear mode and repaired using early-strength concrete with high-fluidity and carbon fiber reinforced polymers (CFRP). After about four days, the repaired specimens were tested to failure again. The seismic behavior of the repaired specimens was evaluated and compared to the original specimens. Test results indicate that the proposed repair technique is highly effective. Both shear strength and lateral displacement of the repaired piers increased when compared to the original specimens, and the failure mechanism of the piers shifted from flexural-shear failure to ductile flexural failure. Finally, a simple design model based on the Seible formulation for post-earthquake repair design was compared to the experimental results. It is concluded that the design equation for bridge pier strengthening before an earthquake could be applicable to seismic repairs after an earthquake if the shear strength contribution of the spiral bars in the repaired piers is disregarded and 1.5 times more FRP sheets is provided. | Sun Zhiguo Wang Dongsheng Du Xiuli Si Bingjun | 2011 | Earthquake Engineering and Engineering Vibration2011，10，4： | 7 |
| 3 | Experimental research and finite element analysis of bridge piers failed in flexure-shear modes显示文摘In recent earthquakes,a large number of reinforced concrete (RC) bridges were severely damaged due to mixed flexure-shear failure modes of the bridge piers.An integrated experimental and finite element (FE) analysis study is described in this paper to study the seismic performance of the bridge piers that failed in flexure-shear modes.In the first part,a nonlinear cyclic loading test on six RC bridge piers with circular cross sections is carried out experimentally.The damage states,ductility and energy dissipation parameters,stiffness degradation and shear strength of the piers are studied and compared with each other.The experimental results suggest that all the piers exhibit stable flexural response at displacement ductilities up to four before exhibiting brittle shear failure.The ultimate performance of the piers is dominated by shear capacity due to significant shear cracking,and in some cases,rupturing of spiral bars.In the second part,modeling approaches describing the hysteretic behavior of the piers are investigated by using ANSYS software.A set of models with different parameters is selected and evaluated through comparison with experimental results.The influences of the shear retention coefficients between concrete cracks,the Bauschinger effect in longitudinal reinforcement,the bond-slip relationship between the longitudinal reinforcement and the concrete and the concrete failure surface on the simulated hysteretic curves are discussed.Then,a modified analysis model is presented and its accuracy is verified by comparing the simulated results with experimental ones.This research uses models available in commercial FE codes and is intended for researchers and engineers interested in using ANSYS software to predict the hysteretic behavior of reinforced concrete structures. | Sun Zhiguo Si Bingjun Wang Dongsheng Guo Xun | 2008 | Earthquake Engineering and Engineering Vibration2008，7，4： | 6 |
您所在的机构暂未开通此部分的功能，请联系管理员