| 1 | Processing map for hot working of SiC_p/7075 Al composites显示文摘The hot deformation behaviour of 7075 aluminium alloy reinforced with 10%of SiC particles was studied by employing both'processing maps'and microstructural observations.The composite was characterized by employing optical microscope to evaluate the microstructural transformations and instability phenomena.The material investigated was deformed by compression in the temperature and strain rate ranges of 300-500℃and 0.001-1.0 s-1,respectively.The deformation efficiency was calculated by strain rate sensitivity(m)values obtained by hot compression tests.The power dissipation efficiency and instability parameters were evaluated and processing maps were constructed for strain of 0.5.The optimum domains and instability zone were obtained for the composites.The optimum processing conditions are obtained in the strain rate range of 0.1-0.9 s-1and temperature range of 390-440 ℃with the efficiency of 30%. | M.RAJAMUTHAMILSELVAN S.RAMANATHAN R.KARTHIKEYAN | 2010 | Transactions of Nonferrous Metals Society of China2010，20，4： | 10 |
| 2 | Hot Deformation Behavior of 2124 Al Alloy显示文摘粉末冶金学生产的 2124 艾尔合金的机械行为在不同温度和紧张率与耐压试验被调查。测试从 0.001 s~ 在 300 deg C-500 deg C 并且以紧张率的温度范围被执行(-1) to1.0 s^(-1) 。压缩流动曲线与紧张展出了起始的锋利的增加,由单调的变硬列在后面。最大的压力与减少的紧张率和增加的温度减少了。材料的热变丑特征用处理地图被学习。安全和不安全的政体的领域通过微结构被鉴别并且验证检查。 | S.Ramanathan R.Karthikeyan V.Deepak Kumar G.Ganesan | 2006 | Journal of Materials Science & Technology2006，22，5： | 9 |
| 3 | 用热加工图研究铸态和挤压态ZE41A镁合金的热加工性能(英文)显示文摘采用热加工图研究铸态和挤压态ZE41A镁合金的热变形行为和组织演变。在温度250-450℃,应变速率0.001-1.0s-1的条件下,对铸态和挤压态合金进行抗压测试,建立热加工图。通过显微组织观察确定动态再结晶和不稳定区域。挤压态ZE41A镁合金比铸态合金具有较高的流变应力,较高的能量损耗率和较小的不稳定区域。由于晶粒的细化、材料孔隙度的降低、硬化和强化,挤压态镁合金具有良好的热加工性能。 | S.ANBU SELVAN S.RAMANATHAN | 2011 | Transactions of Nonferrous Metals Society of China2011，21，2： | 6 |
| 4 | 纳米SiC颗粒增强Ti-6Al-4V基复合材料的制备和力学性能(英文)显示文摘采用粉末冶金技术制备含不同质量分数(0,5%,10%和15%)纳米SiC颗粒增强的Ti-6Al-4V(Ti64)金属基复合材料(MMCs),研究添加纳米SiC颗粒对复合材料力学性能如硬度和抗压强度的影响。结果表明,当压缩载荷为6.035 MPa时,复合材料具有最佳的相对密度(93.33%)。SEM显微组织观察结果表明,Ti64/5%SiC_p复合材料的润湿性和结合力得到了提高。采用X射线衍射技术研究Ti64/SiC_p复合材料中纳米SiC颗粒含量对其相组成的影响,并分析其力学性能与相组成的关系。含10%和15%SiC_p的复合材料由于脆性界面反应产生了新相,此新相对复合材料的强度和硬度不利。Ti64/5%SiC_p金属基复合材料的抗压强度和硬度较高,因此5%SiC_p是此复合材料的最佳含量。 | G.SIVAKUMAR V.ANANTHI S.RAMANATHAN | 2017 | Transactions of Nonferrous Metals Society of China2017，27，1： | 1 |
您所在的机构暂未开通此部分的功能，请联系管理员