	1	Effects of caliber rolling on microstructure and room temperature tensile properties of Mge3Ale1Zn alloy显示文摘Mge3Ale1Zn(AZ31)alloy was caliber rolled isothermally in the temperature range of 250e450C to develop fine grains of 3.6e12.5 mm.The stressestrain curves obtained from tensile tests at room temperature were found to vary with the temperature employed in caliber rolling.Maximum tensile strength of 290 MPa and ductility of 13.5%were obtained upon caliber rolling at 300C as compared to 188 MPa and 15.2%,respectively,in the mill-rolled condition.The variations in tensile properties are explained by the concomitant grain size,texture and twins obtained as a function of caliber rolling temperature.	R.L.Doiphode S.V.S.Narayana Murty N.Prabhu B.P.Kashyap	2013	Journal of Magnesium and Alloys2013，1，2：	7
	2	Grain growth in calibre rolled Mg-3Al-1Zn alloy and its effect on hardness显示文摘Calibre rolling of Mg-3Al-1Zn alloy at 300℃ led to development of fine grain size of 3μm.Subsequent annealing,from 5 to 6000 minutes at 300-450℃,revealed faster grain growth initially up to 60 minutes,which became sluggish on prolonged annealing.The time exponent for grain growth kinetics(n)suggests bi-linear behaviour with n=0.11 and 0.008 over these time scales.The activation energy,based on various n values,varied over wide ranges that made the understanding of the mechanisms for grain growth difficult.This problem is explained by concurrent evolution of texture and grain boundary structure.The effect of grain growth on hardness at ambient temperature was found to follow the H-P type relationship.	R.L.Doiphode S.V.S.Narayana Murty N.Prabhu B.P.Kashyap	2015	Journal of Magnesium and Alloys2015，3，4：	4

返回顶部每页显示：

共1页首页上一页第1页下一页末页 /1 跳转

goolge学术搜索-维普

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费