| 3 | Review on Hydrogen Embrittlement of Press-hardened Steels for Automotive Applications显示文摘Press-hardened steel(PHS)with an ultimate tensile strength(UTS)of 1500 MPa has been widely used in automotive body-in-white in the last two decades,due to its ultra-high strength and excellent formability that is achieved by hot stamping process.However,the application of PHS with UTS exceeding 1500 MPa in automotive industry could be deferred due to the increased risk of hydrogen embrittlement.To reduce this kind of risk,recent research efforts have been focused on various ways to optimize the microstructure of PHS.The present review intends to summarize these efforts,to highlight present solutions to address hydrogen embrittlement,and to shed light on directions for future improvement.The influence of microstructure on the hydrogen embrittlement of PHS has been discussed in terms of both the steel substrate and the surface condition.The substrate part covers the influence of martensite,carbides,inclusions,and retained austenite,while the surface part covers decarburization and oxidation,pre-coating,and trimming. | Z.Wang Q.Lu Z.H.Cao H.Chen M.X.Huang J.F.Wang | 2023 | Acta Metallurgica Sinica(English Letters)2023，36，7： | 0 |
| 4 | STUDY ON THE VARIATION MECHANISM OF CARBON CONTENT OF LIQUID IRON IN MELTING GASIFIER显示文摘This paper studied the changing principles of carbon content in direct reduction iron(DRI) and liquid iron in the COREX melting gasifier. Under the normal workingconditions of experimental equipment, liquid nitrogen was poured into the meltinggasifier from its tuyere to cool down quickly. And then seven cross sections were madeto study the carburization reaction and its characteristics of the solid iron and theliquid iron, and also the reaction of carbon between the slag and the metal. Accordingto the results, the influences of the thickness of the semi-coke layer and the temperatureon the carbon content of liquid iron in the COREX melting gasifier were confirmed. | Q.Lu L.F Sun Y.Xu Q.F.Chan | 2003 | Acta Metallurgica Sinica(English Letters)2003，16，2： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员