| 1 | Growth process and short chain alcohol separation performance of fluoride-containing NaY zeolite membrane显示文摘Growth process of the NaY zeolite membranes was investigated by fluoride-containing precursor synthesis gel.Compared with the fluoride-free precursor synthesis gel,the irregular NaY zeolite crystals were dissolved into amorphous by the fluoride-containing precursor synthesis gel initially,the amorphous contained the Y-type zeolite characteristic bands by the IR characterization.The fine square NaY zeolite crystals arose from the amorphous,which were accumulated and gradually grew into a dense NaY zeolite layer on the support surface after 6.5 h.Because the excessive NaY zeolites were dissolved by the strong alkaline and fluoride-containing precursor synthesis gel,there was plenty of amorphous on NaY zeolites layer for prolonging the crystallization time.The assynthesized NaY zeolite membranes had a good separation performance and repeatability for separation of 10 wt%methanol(MeOH)/methyl methacrylate(MMA) mixture by pervaporation,the flux and separation factor were(1.27 ± 0.07) kg·M^(-2)·h^(-1) and(4900 ± 1500) at 323 K,respectively.Besides,the NaY zeolite membranes were applied to separate the other short chain alcohol from the various alcohol/organic ester and alcohol/organic ether mixtures,the NaY zeolite membranes showed high short chain alcohol perm-selectivity. | Xiaopan Chen Meihua Zhu Sitong Xiang Tian Gui TingWu Yuqin Li NaHu Izumi Kumakiri Xiangshu Chen Hidetoshi Kita | 2021 | Chinese Journal of Chemical Engineering2021，34，1： | 1 |
您所在的机构暂未开通此部分的功能，请联系管理员