| 1 | 功能梯度铜基复合材料的制备及干摩擦磨损性能(英文)显示文摘采用水平离心铸造工艺,制备功能梯度铜基复合材料,并对其非润滑滑动性能进行了研究.采用基于Taguchi的L27正交实验对石墨颗粒含量较高的空心圆柱铸件内壁厚度的磨损速率和摩擦系数进行分析.直接或间接影响磨损速率的工艺参数包括:施加的载荷(15,25和35 N)、滑动速度(1.5,2.5和3.5 m/s)和滑动距离(750,1500和2250 m).磨损速率和摩擦系数与施加的载荷和滑动距离呈比例的依赖性,而在中间滑动速度期间表现出下降.信噪比在'较小-较好'的基础上预测最小三波条件.方差分析量化参数的影响及其相互作用.采用回归分析对实验数据进行验证.在磨损表面分析过程中,通过显微镜和扫描电子显微镜发现磨损机制和机械混合层的形成. | N.RADHIKA Manu SAM | 2019 | Journal of Central South University2019，26，11： | 4 |
| 2 | Influence of carbide ceramic reinforcements in improving tribological properties of A333 graded hybrid composites显示文摘Aluminium hybrid functionally graded metal matrix composites(FGMMCs),meet growing demands for supreme tribo-mechanical performance in automotive and aviation industry.This research experimentally compares the influence of carbide ceramics(B_(4)C,SiC,TiC)as reinforcements,in improving reciprocating tribology performance and mechanical strength of A333 hybrid composites against alloy.Hollow cylindrical samples of A333/6 wt%B_(4)C/4 wt%TiC and A333/6 wt%B_(4)C/4 wt%SiC hybrid FGMMCs were developed using horizontal centrifugal casting.Metallography analysis on both composites revealed increasing ceramic gradient distribution towards outer composite wall.Particle rich zone of A333/B_(4)C/SiC hybrid FGMMC showed maximum micro-hardness(198.9 HV)and tensile strength(267.9 MPa).Elemental mapping confirmed effective distribution of ceramics and detected elemental composition of both composites.Particle rich layer of A333/B_(4)C/SiC hybrid FGMMC exhibited improved wear resistance in comparison with all three layers of A333/B_(4)C/TiC hybrid FGMMC and alloy.Third-body abrasion and tribo-chemical wear were the predominant mechanisms revealed for both composites during worn surface analysis. | Manu Sam N.Radhika | 2022 | Defence Technology(防务技术)2022，18，7： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员