| 1 | INTERFACIAL STRUCTURE AND PHASE REACTION IN SiC/NiCr ALLOY JOINT显示文摘Bonding of SiC to SiC using Ni and Ni - 25at%Cr foils was performed at high temperature.Interface structures and reaction phases were investigated by EPMA analyses and XRD diffraction method, re- spectively. At a bonding temperature of 1273K Ni reacts with SiC and forms various Ni silicides con- taining graphite baside SiC. Ni3Si without graphite was formed at Ni side.The interface structure of SiC/Ni joint was SiC/Ni2Si + C/Ni31 Si12 + G/Ni3 Si/Ni. At the interface between SiC and Ni- 25at%Cr alloy the Ni silicide was only Ni2Si at the same bonding temperature,and further(Cr, Ni)7 (Si, C)3 carbide was formed between Ni silicide + graphite zone and Ni - 25at%Cr alloy.The interface structure of SiC/Ni - 25at%Cr alloy was SiC/Ni2Si + C/(Cr, Ni)7 (Si, C)3+Ni(ss. Cr, Si)/Ni - 25at%Cr. | J. C. Feng M. Naka J. C. Schuster(School of Materials Science and Engineering, Harbin Institute of Technology, Harbin, 150001, China Joining and Welding Research Institute, Osaka University, Mihogaoka 11 - 1, Ibaraki, Osaka 567, Japan Institute of P | 2000 | Acta Metallurgica Sinica(English Letters)2000，13，1： | 6 |
您所在的机构暂未开通此部分的功能，请联系管理员