| 1 | Microstructural features of Ti-6Al-4V manufactured via high power laser directed energy deposition under low-cycle fatigue显示文摘Laser additive manufacturing(LAM)technique has unique advantages in producing geometrically complex metallic components.However,the poor low-cycle fatigue property(LCF)of LAM parts restricts its widely used.Here,the microstructural features of a Ti-6 Al-4 V alloy manufactured via high power laser directed energy deposition subjected to low-cycle fatigue loading were studied.Before fatigue loading,the microstructure of the as-deposited parts was found to exhibit a non-homogeneous distribution of columnar prior-βgrains(200-4000μm)at various scanning velocities(300-1500 mm/min)and relatively coarseα-laths(1.0-4.5μm).Under cyclic loading,fatigue microcracks typically initiated within the alignedαphases in the preferred orientation(45°to the loading direction)at the surface of the fatigue specimens.Fatigued Ti-6 Al-4 V exhibited a single straight dislocation character at low strain amplitudes(<0.65%)and dislocation dipoles or even tangled dislocations at high strain amplitudes(>1.1%).In addition,dislocation substructure features,such as dislocation walls,stacking faults,and dislocation networks,were also observed.These findings may provide opportunities to understand the fatigue failure mechanism of additive manufactured titanium parts. | Y.M.Ren X.Lin H.O.Yang H.Tan J.Chen Z.Y.Jian J.Q.Li W.D.Huang | 2021 | Journal of Materials Science & Technology2021，，24： | 3 |
您所在的机构暂未开通此部分的功能，请联系管理员