| 1 | INFLUENCE OF PULSED MAGNETIC FIELD ON MICROSTRUC-TURES AND MACRO-SEGREGATION IN 2124 Al-ALLOY显示文摘The structures and macro-segregation of 2124 Al-alloy were studied when a pulsedmagnetic field (PMF) was applied during solidification. It is found through experi-ments that a remarkable change occurs in the solidification structures of 2124 Al-alloyunder pulsed magnetic field. The eutectic phase at grain boundaries change from thickcontinuous eutectic network to thin discontinuous one, and the distribution of soluteelements was also homogenized. The typical negative segregation phenomenon of Cu incommon solidification condition was restrained, and the segregation of Mg decreased. | C.Y.Ban,J.Z.Cui,Q.X.Ba,G.M.Lu and B.J.ZhangP.O. Box 317, The Key Laboratory of Electromagnetic Processing of Materials, Ministry of Education, Northeastern University, Shenyang 110004, China Manuscript received 10 October 2001 | 2002 | Acta Metallurgica Sinica(English Letters)2002，15，4： | 19 |
| 2 | EVOLUTION OF AS-CAST MICROSTRUCTURES OF 356 ALUMINIUM ALLOY CAST BY LIQUIDUS CASTING显示文摘A new method (liquidus casting) was used for 356 Al alloy semi-solid slurry mak-ing. The structures of 356 Al alloy cast by a Fe mould and semi-continuous castingmachine at different temperatures were investigated. How the globular grains formwas also discussed. The results show that either being cast by single Fe mould orsemi-continuous machine, the microstructures are not conventional dendrites but fineand net-globular grains. The average grain size is smaller than 30μm and suitableenough for thixoforming, meanwhile it can improve the mechanical properties of fol-lowing products. Under the suitable casting velocity and cooling intensity, most ofglobal grains prolong their global growth and collide with each other before dendriticgrowth because of the large amount of the nucleation sites. | J.Dong G.M.Lu J.Z.Cui Z.H.Zhao | 2003 | Acta Metallurgica Sinica(English Letters)2003，16，1： | 5 |
您所在的机构暂未开通此部分的功能，请联系管理员