| 1 | Luminescence properties of near-UV excitable yellow-orange light emitting warm CaSrAl_2SiO_7:Sm^(3+) phosphors显示文摘Single-phase CaSrAl_2 SiO_7:Sm^(3+) phosphors were synthesized by traditional high temperature solid state reaction method. Formation of samples and phase analysis were confirmed by X-ray diffraction technique. Morphology was done by field emission scanning electron microscopy and elemental compositions were confirmed by energy dispersive X-ray analysis. Present phosphors have tetragonal crystallography with space group P42_1 m. Average crystallite size was calculated by using Scherrer and Williamson-Hall method. Photoluminescence study of CaSrAl_2 SiO_7:Sm^(3+) phosphor was investigated.Under different excitation wavelengths, PL spectra consist of four emission bands at 564, 570, 601 and650 nm. The emission bands located at 564 and 570 nm are associated with the transition ~4 G_(5/2)→~6 H_(5/2)while emission bands at 601 and 650 nm are due to ~4 G_(5/2)→~6 H_(7/2) and ~4 G_(5/2)→~6 H_(9/2),respectively.Intense emission was obtained when phosphor was excited under 404 nm wavelength. Non-radiative energy transfer process involved in concentration quenching, was also discussed. CIE coordinate is found in yellow-orange region, hence CaSrAl_2SiO_7:Sm^(3+) phosphors emit yellow-orange light when efficiently excited by near UV(~400 nm) LED chip. Color purity and CCT of the phosphor were determined; CCT suggests that present phosphor is a good candidate as a warm yellow-orange color emitting phosphor. Effect of different heating rates and different UV exposure time on the TL glow curve of the phosphor was investigated. Activation energies and kinetic parameters for different traps were calculated by using peak shape method. TL emission spectrum was also recorded. Present article explains all the possible mechanisms associated with luminescence process in CaSrAl_2 SiO_7:Sm^(3+) phosphors. | Shweta Sharma Nameeta Brahme D.P.Bisen Pradeep Dewangan | 2019 | Journal of Rare Earths2019，37，4： | 3 |
您所在的机构暂未开通此部分的功能，请联系管理员