| 1 | The relation between ductility at high temperature and solid solution in Mg alloys显示文摘This work investigates the effect of solid solution on ductility and on the activation of individual deformation mechanisms at moderate temperatures and at quasi-static strain rates in Mg-Zn and Mg-Al alloys. With that aim, four solid solution Mg-Zn and Mg-Al binary alloy ingots containing 1 and 2 wt.% solute atoms were subjected to hot rolling and subsequent annealing to generate polycrystals with similar average grain size and basal-type texture for each composition. The activity of the different slip systems after tensile testing at 150°C and at 250°C was evaluated in pure Mg and in the alloys by EBSD-assisted slip trace analysis. In addition, segregation of Zn and Al atoms at grain boundaries during the thermo-mechanical processing was characterized by HAADF-STEM and EDX. It was found that while the addition of Al and Zn atoms to pure Mg does not lead to major changes in the mechanical strength at the investigated temperatures, it does enhance ductility significantly, especially at 250℃. Our results show that this increase in ductility cannot be attributed to a higher activation of non-basal systems in the alloys, as reported earlier, as the incidence of non-basal systems is indeed considerably higher in pure Mg. This work suggests, on the contrary, that the ductility increase may be attributed to the presence of a more homogenous basal activity in the alloys due to a lower degree of orientation clustering, to grain boundary solute segregation, and to a higher slip diffusivity at grain interiors. | D.F.Shi C.M.Cepeda-Jiménez M.T.Pérez-Prado | 2022 | Journal of Magnesium and Alloys2022，10，1： | 2 |
| 2 | High-temperature fatigue strength of grain boundaries with different misorientations in nickel-based superalloy bicrystals显示文摘Nickel-based single-crystal superalloys are widely used in the manufacture of aeroengine turbine vanes for their excellent high-temperature performance. Low-angle grain boundaries (LAGBs) will be generated inevitably during their manufacture, which are often characterized by grain boundary misorientation (GBM) and will weaken the mechanical properties of superalloys. However, the relationship between GBM and the fatigue properties of superalloys at elevated temperatures has seldom been investigated due to the difficulty in the sample preparation and experiment process. Based on six kinds of bicrystals with different tilt LAGBs made by a second-generation single-crystal superalloy, the effects of misorientation on the grain boundary microstructure and fatigue properties (980 °C) of superalloys were studied systematically in this work. It is found that, with the increase of GBM, the GB precipitates combined with the cast micropores increase monotonically, accordingly both the fatigue life and fatigue strength decrease successively. Fatigue fracture observations show that the cracks of all the bicrystals initiated from the cast micropores at GBs, and then propagated along the GBs. Therefore, the coupling effect of cast micropores and GBM on the fatigue damage mechanisms of the bicrystals are evaluated according to their hindering degrees on the piled-up dislocations. Combining with a hysteresis energy model, a quantitative fatigue strength prediction model of superalloys is established and is well verified by abundant experimental data. This study could provide guidance for fatigue performance prediction and structural design of superalloys. | D.F.Shi Z.J.Zhang Y.H.Yang Y.Z.Zhou R.Liu P.Zhang Z.F.Zhang | 2023 | Journal of Materials Science & Technology2023，，23： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员