| 1 | Characterization of mechanical properties of aluminum cast alloy at elevated temperature显示文摘The tensile response, the low cycle fatigue(LCF) resistance, and the creep behavior of an aluminum(Al) cast alloy are studied at ambient and elevated temperatures.A non-contact real-time optical extensometer based on the digital image correlation(DIC)is developed to achieve strain measurements without damage to the specimen. The optical extensometer is validated and used to monitor dynamic strains during the mechanical experiments. Results show that Young's modulus of the cast alloy decreases with the increasing temperature, and the percentage elongation to fracture at 100℃ is the lowest over the temperature range evaluated from 25℃ to 300℃. In the LCF test, the fatigue strength coefficient decreases, whereas the fatigue strength exponent increases with the rising temperature. The fatigue ductility coefficient and exponent reach maximum values at 100℃. As expected, the resistance to creep decreases with the increasing temperature and changes from 200℃ to 300℃. | Shuiqiang ZHANG Yichi ZHANG Ming CHEN Yanjun WANG Quan CUI Rong WU D.AROLA Dongsheng ZHANG | 2018 | Applied Mathematics and Mechanics(English Edition)2018，39，7： | 4 |
| 2 | Importance of aging to dehydration shrinkage of human dentin显示文摘There is an increase in the mineral content of human dentin with aging.Due to the consequent changes in the mineral to the collagen ratio,this process may influence the degree of hydrogen bonding that occurs with the loss of water and the extent of shrinkage as a result of dehydration.Thus,the objective of this investigation is to quantify the differences in the dehydration shrinkage of human dentin with patient age.Specimens of coronal dentin are prepared from the molars of young(23 age 34) and old(52 age 62) patients,and then maintained in storage solutions of water or hanks balanced salt solutions(HBSS).Dimensional changes of the dentin specimens occurring over periods of free convection are evaluated by using the microscopic digital image correlation(DIC).The results distinguish that the shrinkage of the young dentin is significantly larger than that of the old dentin,regardless of the orientation and period of the storage.The strains parallel to the tubules increase with proximity to the dentin enamel junction(DEJ),whereas the shrinkage strains in the transverse direction are the largest in the deep dentin(i.e.,near the pulp).The degree of anisotropy in the shrinkage increases from the pulp to the DEJ,and is the largest in the young dentin. | 汪饶饶 毛霜霜 E.ROMBERG D.AROLA 张东升 | 2012 | Applied Mathematics and Mechanics(English Edition)2012，33，3： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员