| 1 | Effect of Nitrogen Content on Microstructures and Mechanical Properties of WB_2(N) Films Deposited by Reactive Magnetron Sputtering显示文摘In the present study,WB_2(N) films are fabricated on silicon and YG8 substrates at different N_2 pressures by reactive magnetron sputtering.The influence of N_2 partial pressure(P_(N2)) on the film microstructure and characteristics is studied systematically,including the chemical composition,crystalline structure,residual stress,surface roughness as well as the surface and the cross-section morphology.Meanwhile,nano-indentation and ball-on-disk tribometer are performed to analyze the mechanical and tribological properties of the films.The results show that the addition of nitrogen apparently leads to the change of the structure from(1 0 1) to(0 0 1) orientation then to the amorphous structure with the formation of BN phase.And the addition of nitrogen can greatly refine the grain size and microstructure of the films.Furthermore,the residual stress of the film is also found to change from tensile to compressive stress as a function of P_(N2),and the compressive stress increases with P_(N2),The WB_2(N) films with small nitrogen content,which are deposited at P_(N2) of 0.004 and 0.006 Pa,exhibit better mechanical,tribological and corrosion properties than those of other films.Further increase of nitrogen content accelerates the formation of BN phase and fast decreases the film hardness.In addition,the large N_2 partial pressure gives rise to the target poisoning accompanied by the increase of the target voltage and the decrease of the deposition rate. | Y.M.Liu D.Y.Deng H.Lei Z.L.Pei C.L.Jiang C.Sun J.Gong | 2015 | Journal of Materials Science & Technology2015，31，12： | 5 |
| 3 | Relationship between the fatigue behavior and grain structures of an as-extruded Mg-6.2%Zn-0.6%Zr(in wt.%)alloy显示文摘Through investigating the tension-tension fatigue behavior of an as-extruded Mg-6.2 wt.%Zn-0.6 wt.%Zr(ZK60)alloy,it revealed that the determined fatigue strength at 107 cycles was quite sensitive to the grain structure.Among them,the fine grain structure had the highest fatigue strength of 130 MPa,whereas the typical“bi-modal”grain structure had the lowest fatigue strength of 110 MPa.Failure analysis demon-strated that for the fine grain structure,fatigue cracks preferentially nucleated at grain boundaries.For the“bi-modal”and coarse grain structures,the fatigue crack initiation was dominated by the cracking along slip bands. | B.J.Wang D.K.Xu C.L.Jiang L.Y.Sheng E.H.Han | 2023 | Journal of Materials Science & Technology2023，，18： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员