General synthesis of high-performing magneto-conjugated polymer core-shell nanoparticles for multifunctional theranostics

查看全文 作　　者：Hao [1,2,3]Yan;Lingyun [1,2]Zhao;Wenting [4]Shang;Zhongqun [1,2]Liu;Wensheng [1,2]Xie;Cai [1,2]Qiang;Zhiyuan [2]Xiong;Ranran [1,2]Zhang;Baohua [3]Li;Xiaodan [1,2]Sun;Feiyu [1,3]Kang

机构地区：[1]State Key Laboratory of New Ceramics and Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China;[2]Key Laboratory of Advanced Materials of Ministry of Education of China, Tsinghua University, Beijing 100084, China;[3]Engineering Laboratory for Functionalized Carbon Materials, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China;[4]Key Laboratory of Molecular Imaging, Institute of Automation, Chinese Academy of Sciences, Beijing 100190, China

出　　处：《Nano Research》索引2017年第10卷第2期,共14页

摘　　要：最近,增加注意作为 theranostic 平台被付了到结合磁电机的聚合物核心壳 nanoparticles (NP ) 。然而,表面活化剂的利用和有在合成的潜在的毒性的额外的氧化剂,为磁性的 NP ( MNP )@的各种各样的类型的控制合成的一般方法的缺乏结合了聚合物 NP ,并且获得平衡磁电机光的性质的困难极大地在 theranostics 限制了结合磁电机的聚合物的应用。我们发展了一在里面没有额外的表面活化剂和氧化剂的 situ 表面聚合方法综合有平衡、突出的磁电机光的性质的 MNP@polypyrrole (PPy ) NP。有一种可调节的尺寸,不同形状,和控制的壳厚度的 MNP@PPy NP 用这个方法被获得。方法被扩大综合另外的结合 MNP 的聚合物核心壳 NP,例如 MNP@polyaniline 并且 MNP@poly (3,4-ethylenedioxythiophene ): poly (4-styrenesulfonate )(PEDOT : PSS ) 。我们根据我们的试验性的结果讨论建议方法的形成机制。最后,使用光并且获得的 MNP@PEDOT 的磁性: PSS NP,在 vivo,多模式的指导成像的过高热在老鼠被导致,完成优秀肿瘤脱离治疗学的效果。我们的工作为在生物医学的域里扩大结合 MNP 的聚合物核心壳 NP 的应用程序是有益的。 关键词：氧化铁 POLYPYRROLE PHOTOTHERMAL 磁性过高热 poly (3,4-ethylenedioxythiophene ) :poly (4-styrenesulfonate )(PEDOT : PSS )

相关文献

参考文献（45）
引证文献（2）
耦合文献（0）

参考文献(45)

引证文献(2)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

General synthesis of high-performing magneto-conjugated polymer core-shell nanoparticles for multifunctional theranostics

参考文献(45)

引证文献(2)

用户提示