| 1 | The effects of orientation control via tension-compression on microstructural evolution and mechanical behavior of AZ31 Mg alloy sheet显示文摘The grain orientation control via twinning activity on deformation features is of great significance to offer a key insight into understanding the deformation mechanism of Mg alloy sheets.The{10–12}twinning were performed by pre-strain paths,i.e.,tension(6%)and compression(5%)perpendicular to the c-axis along extrusion direction(ED),to investigate the microstructural evolution and mechanical properties of AZ31 Mg alloy sheets.The distinction in the texture evolution and strain hardening behavior was illustrated in connection with the pre-strain paths for the activities of twinning and slip.The result shows that the activation of the deformation mode was closely bound up with the grain orientation and the additional applied load direction.The{10–12}twin-texture components with c-axis//ED were generated by precompression,which can provide an appropriate alternative to accommodate the thin sheet thickness strain and enhance the room temperature formability of Mg alloy sheet. | Qingshan Yang Bin Jiang Bo Song Zujian Yu Dewei He Yanfu Chai Jianyue Zhang Fusheng Pan | 2022 | Journal of Magnesium and Alloys2022，10，2： | 4 |
| 2 | 稀土Y元素对铸态镁合金组织与力学性能的影响显示文摘采用熔炼工艺制备了Mg-2.0Zn-0.2Ca与Mg-2.0Zn-0.2Ca-2Y合金,研究了两种合金的铸态组织及力学性能。结果表明,Y元素的添加细化了Mg-2.0Zn-0.2C合金的铸态组织。Mg-2.0Zn-0.2Ca合金主要由α-Mg与少量Mg7Zn3相组成,添加2wt%的Y后,改变了Zn在Mg基体中的固溶度,降低了其固溶强化效果,同时组织中形成了I相和W相。添加Y元素后,合金的规定塑性延伸强度升高,从41.0 MPa升高到50.6 MPa;伸长率降低,从12.6%降低到4.0%。 | 张旭东 索转霞 魏博鑫 王辛 曹国剑 | 2020 | 金属热处理2020，45，10： | 2 |
| 3 | Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr稀土镁合金室温包套压缩变形行为及变形机制显示文摘在室温条件下对固溶处理的热挤压态Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr稀土镁合金分别进行单轴压缩与包套压缩实验,采用光学显微(OM)、电子背散射衍射(EBSD)、X射线衍射(XRD)和透射电子显微(TEM)等研究了该合金在变形后的微观组织。合金在单轴压缩条件下的最大变形量为18%,而在包套压缩条件下的最大变形量高达32%。结果表明:该合金在两种变形条件下的微观组织演化规律类似,即均会因协调塑性变形的需要而产生{1012}拉伸孪晶和{1121}拉伸孪晶,且前者的数量多于后者。同时,在变形过程中晶粒c轴向压缩方向的聚集程度逐渐增大。在18%变形量条件下,包套压缩试样的位错密度(0.2728 nm^(−2))明显高于单轴压缩试样的位错密度(0.1796 nm^(−2));在18%变形量条件下的单轴压缩试样中,主要激活的位错类型为〈a〉位错,而〈c+a〉位错数量较少;而在包套压缩试样中,〈c+a〉位错被大量激活来承载塑性应变,进而导致Mg-8.5Gd-4.5Y-0.8Zn-0.4Zr稀土镁合金的室温塑性显著提升。 | 章懿清 汪丽佳 胡励 何曲波 周涛 时来鑫 李明骜 | 2023 | 中国有色金属学报2023，33，7： | 2 |
| 4 | 孪晶取向对AZ31镁合金板材各向异性的影响显示文摘沿AZ31镁合金商用板材TD方向预轧制引入孪晶结构。通过拉伸试验考察孪晶取向对镁合金板材各向异性的影响。结果表明商用AZ31板材具有强的基面织构和较小的平面各向异性。沿TD方向的侧轧可以产生大量的拉伸孪晶,并产生c轴//TD的孪晶取向。在应变量8%并退火后的AZ31板材中形成了单一的c轴//TD织构。孪晶取向的产生极大地降低了TD方向和45°方向的拉伸屈服强度,进而导致了强的平面各向异性。此外,c轴//TD织构的形成会提高板材协调厚度方向变形的能力,从而极大地降低板材的塑性应变比。 | 余虹妮 申梦鑫 杜治文 宋波 | 2023 | 热加工工艺2023，52，1： | 1 |
| 5 | Post deformation analysis of the ballistic impacted magnesium alloys,a short-review显示文摘From the mechanistic point of view,magnesium alloys are lightweight materials and are receiving increasing attention in the past several years in various fields.Prof.Liang Zhen from Harbin Institute of Technology,China and the United State military are showing keen interest in the development of magnesium alloys as ballistic resistant material.However,their use is still limited owing to low ductility,low formability,and average mechanical properties.The magnesium alloys components must withstand the shockwave under hypervelocity ballistic impact.The ballistic testing can produce gradient variations of the strain and stress-energy away from the crater,and useful for the development of these alloys in the military and aerospace industry.Therefore,the present review article shed light on the post deformation analysis of the Mg alloys subjected to the different projectiles under ballistic impact,and the underlying mechanisms were discussed.In the end,some important issues regarding the ballistic impact and further studies in this field were proposed. | Abdul Malik Yangwei Wang Cheng Huanwu Faisal Nazeer Muhammad Abubaker Khan | 2021 | Journal of Magnesium and Alloys2021，9，5： | 1 |
| 6 | 基于弯曲定径带模具挤压的Mg-3Al-1Zn合金力学性能优化显示文摘设计了一种采用弯曲定径带模具的新型非对称挤压工艺(TBE),用以改善Mg-3Al-1Zn合金板材的力学性能和成形性能。运用有限元分析揭示了挤压过程中的应变、温度等状态变量的分布。结果表明,在TBE模具的模口处,应变沿板面法向(ND)呈梯度分布,这导致挤压板材显微组织的厚向梯度分布,同时得到TD择优取向的织构,少量基面取向晶粒向挤压方向(ED)偏转。与传统挤压相比,TBE过程中产生更多挤压热,模腔内温度更高,使大量非基面滑移开启,导致板材TD择优取向织构的形成。通过改善织构,TBE板材的塑性和弯曲性能均得到明显提升,沿45°方向的伸长率达到33%,弯曲角度达到83.5°。 | 刘林涛 白生文 蒋斌 何超 王庆航 袁明 黄光胜 张丁非 潘复生 | 2023 | Transactions of Nonferrous Metals Society of China2023，33，10： | 0 |
| 7 | 挤压温度对累积挤压工艺制备的异质结构Mg-Gd合金复合板组织演化和力学性能的影响显示文摘研究挤压温度对累积挤压工艺制备的异质结构Mg-1Gd/Mg-13Gd复合板显微组织和力学性能的影响。结果表明,当挤压温度为330℃时,Mg-1Gd/Mg-13Gd复合板在连续层之间形成明显的晶粒尺寸差异,随着挤压温度从380℃增加到430℃时,这种差异逐渐消失。此外,细晶层中再结晶晶粒的生长速度快于粗晶层。而且,Gd元素的扩散能力随着挤压温度的升高而增强,促进细晶层中析出相的增加和粗化。拉伸测试表明,380℃下的挤压试样具有优异的强度和塑性结合。这主要归因于粗、细晶层之间的不均匀织构、形变诱导强化和硬化的协同作用。细晶层有利于柱面滑移的激活,而粗晶层有利于基面和锥面滑移的激活,尤其是在380℃时更为显著。锥面滑移的激活有助于协调进一步的塑性变形。 | 刘帅帅 刘晗 张宝煊 黄光胜 陈祥 汤爱涛 蒋斌 潘复生 | 2022 | Transactions of Nonferrous Metals Society of China2022，32，7： | 0 |
| 8 | 冷媒辅助搅拌摩擦处理AZ31B镁合金的显微组织演变及力学性能显示文摘传统搅拌摩擦处理(FSP)后的AZ31B镁合金通常表现出强烈的基面织构,导致其强度和塑性匹配较差。本文作者采用冷媒辅助搅拌摩擦处理对AZ31B镁合金进行加工,研究液态二氧化碳冷却剂对搅拌区热循环、显微组织和力学性能的影响。使用液态二氧化碳同步冷却法可显著降低搅拌区的峰值温度并提高冷却速度,搅拌区出现具有大量位错和■孪晶的细晶结构。在不连续动态再结晶、连续动态再结晶和孪晶诱导几何动态再结晶的综合作用下,搅拌区发生显著的晶粒细化。拉伸试验中由于位错和■孪晶产生的交互作用,搅拌区的极限抗拉强度和断后伸长率分别达293 MPa和18.6%,表现出良好的强度和塑性匹配。 | 许楠 任紫科 范越 顾帛坤 沈骏 宋亓宁 赵建华 包晔峰 | 2023 | Transactions of Nonferrous Metals Society of China2023，33，6： | 0 |