题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | 原铁液硅含量对厚大断面球墨铸铁件石墨形态与力学性能的影响显示文摘为研究原铁液硅含量对厚大断面球墨铸铁件凝固组织石墨形态和力学性能的影响,使用高精度热模拟系统,考察了不同硅含量的原铁液经过相同球化孕育工艺处理后在相同凝固条件下获得的厚大断面球墨铸铁件试样的凝固组织石墨形态和力学性能。结果表明,球化孕育工艺相同时,随着原铁液硅含量提高,厚大断面球墨铸铁件石墨形态恶化,力学性能下降。当钇基重稀土球化剂和含Ba孕育剂加入量分别为1.8%和0.4%时,原铁液硅含量控制在1.2%以内,有利于防止厚大断面球墨铸铁件石墨畸变,提高铸件力学性能。 | 黎振华 李言祥 周荣 蒋业华 | 2007 | 铸造2007，56，5： | 8 |
| 2 | Melt Quality Evaluation of Ductile Iron by Pattern Recognition of Thermal Analysis Cooling Curves显示文摘The melt quality of ductile iron can be related to the melt’s thermal analysis cooling curve. The freezing zone of the thermal analysis cooling curve was found to indicate the melt quality of the ductile iron. A comprehensive difference parameter, ?, of the thermal analysis cooling curves was found to be related to the properties of ductile iron melts such as composition, temperature, and graphite morphology. As ? ap- proached 0, the thermal analysis cooling curves were found to come together with all the properties indicat- ing melt quality about the same. A database of thermal analysis cooling curves related to the properties of the ductile iron melts was set up as a basis for a method to accurately evaluate the melt quality of ductile iron by pattern recognition of thermal analysis cooling curves. The quality of a ductile iron melt can then be immediately determined by comparing its thermal analysis cooling curve freezing zone shape to those in the database. | 黎振华 李言祥 周荣 | 2008 | Tsinghua Science and Technology2008，13，2： | 6 |
| 3 | Physical modeling of spent-nuclearfuel container显示文摘A new physical simulation model was developed to simulate the casting process of the ductile iron heavy section spent-nuclear-fuel container.In this physical simulation model,a heating unit with DR24 Fe-Cr-Al heating wires was used to compensate the heat loss across the non-natural surfaces of the sample,and a precise and reliable casting temperature controlling/monitoring system was employed to ensure the thermal behavior of the simulated casting to be similar to the actual casting.Also,a mould system was designed,in which changeable mould materials can be used for both the outside and inside moulds for different applications.The casting test was carried out with the designed mould and the cooling curves of central and edge points at different isothermal planes of the casting were obtained.Results show that for most isothermal planes,the temperature control system can keep the temperature differences within 6 ℃ between the edge points and the corresponding center points,indicating that this new physical simulation model has high simulation accuracy,and the mould developed can be used for optimization of casting parameters of spent-nuclear-fuel container,such as composition of ductile iron,the pouring temperature,the selection of mould material and design of cooling system.In addition,to maintain the spheroidalization of the ductile iron,the force-chilling should be used for the current physical simulation to ensure the solidification of casting in less than 2 h. | Wang Liping Guo Erjun Jiang Wenyong Xue Muyu Liu Dongrong Ren Shanzhi | 2012 | China Foundry2012，9，4： | 5 |
| 4 | Ni对厚大断面球铁显微组织和力学性能的影响显示文摘以不含Ni和含Ni的厚大断面球墨铸铁为研究对象,并对其进行低温两阶段退火处理(760℃+4 h和730℃+4 h)。采用光学显微镜、扫描电镜、电子万能试验机和布氏硬度计等研究了厚大断面球铁试样不同部位的显微组织和力学性能。结果表明:退火处理后,试样的铁素体含量达到了95%以上。随着凝固时间的增加,从试样表面到心部位置,出现了畸形石墨,导致力学性能急剧下降。与未加Ni相比,含0.6%Ni试样的石墨球细小圆整,基体组织得到细化,力学性能明显提高。 | 于明基 王丽萍 冯义成 陈亮 付原科 王长亮 | 2020 | 材料热处理学报2020，41，4： | 2 |
| 5 | 厚大断面球墨铸铁铁液石墨畸变倾向预测研究显示文摘通过考察不同厚大断面球墨铸铁铁液热分析曲线凝固段及其对应6h凝固组织间的关系,运用模式识别原理和数据库技术,提出了浇注前预测其石墨畸变倾向的方法。结果表明,热分析曲线凝固段综合偏差判据W值与6h凝固组织的石墨形态差异间存在明显收敛关系,当W趋于0时,6h凝固组织石墨形态的差别向0趋于收敛;当W足够小时,两条热分析曲线的差别也足够小,其对应的两种球墨铸铁铁液6h凝固组织中石墨形态的差别也足够小;待评估厚大断面球墨铸铁铁液的石墨畸变倾向可用与其热分析曲线形状最相近的另一铁液的6h凝固组织的石墨形态进行预测。 | 黎振华 李言祥 周荣 蒋业华 | 2006 | 铸造2006，55，4： | 2 |
您所在的机构暂未开通此部分的功能，请联系管理员